Agglomerated welding flux SJ601 for stainless steel strip cladding
Specifications:
NB/T47018-2011 GB/T17854-1999 F308-HOCr21Ni10 F309-HlCr24Ni13
F316L-H00Cr19Ni12Mo2
Description:
LH-SJ601 is stainless steel with alkali sintering flux,about 1.8 alkalinity,spherical particles,the particle size 10 to 60 mesh(1.7-0.25mm).It can be used on DC(+) or AC,when using DC(+),the wire to the positive(+),arc busing stability weld forming is smooth and beautiful,pure,deposited metal almost does not increase carbon,with the characteristics of chromium burning less suitable for low carbon and low carbon stainless steel submerged arc welding.
Usage:
when applied to appropriate welding wires such as HOCr21Ni10,HOOCr21Ni10 and HOOCr19Ni12Mo2, It can weld low-carbon steel,super-low carbon steel and highalloy heat-resisting steel,and is fit for multiway welding.
Cautions:
1.The oil soil,moisture,iron rust and other foreign substances must be removed form the welding joint.
2.The welding flux must be baked under 300-500ºC for 2 hours before welding.
(Chemical Composition)(%)
|
SiO2+TiO2 |
Al2O3+MnO |
CaO+MgO |
CaF2 |
S |
P |
|
5-10 |
30-40 |
6-10 |
40-50 |
<=0.06 |
<=0.06 |
(Mechanical Performance of the Deposited Metal)
|
Wires |
Standard Models
GB/T17854-1999 |
бb
(MPa) |
δ5
(%) |
|
HOCr21Ni10 |
F308-HOCr21Ni10 |
≥520 |
≥30% |
|
HOOCr21Ni10 |
F308L-HOOCr21Ni10 |
≥480 |
≥25% |
Packing Details:
Bag:25 KGS/Kraft Bag With Plastic Lining Inside
Pallet:40 Bags(1 Ton)/Plywood Pallet
Container:20-24 Tons/Container
OEM Packing Design Can Be Accept According To Your Requirement
Our service
1)Prime quality+Competitive price+Thoughtful Service=100% Satisfication
2)We can research and produce customerized fluxes according to your different demands.
3)SAW Welding Flux Expert- One Stop Solution For Submerged Arc Welding consumables.
Technical data sheet stainless steel welding wire
AWS A5.9 ER308
Description: The main chemical composition of stainless steel welding wire ER308 is 18Cr-8Ni. The weld metal has good mechanical properties, intergranular corrosion resistance and good crack resistance.
Application: Stainless steel welding wire ER308 can be used for welding austenitic stainless steel of type 18-8, 18-12 and 20-10. It is usually used for welding of similar composition, especially the type of 304.
Chemical Composition of Welding Wire(%)
GV=Guarantee Value
| Test Item |
C |
Mn |
Si |
S |
P |
Cr |
Ni |
Mo |
Cu |
| GV |
≤0.08 |
1.0~2.5 |
0.3~0.65 |
≤0.03 |
≤0.03 |
19.5~22 |
9.0~11.0 |
≤0.75 |
≤0.75 |
| Typical |
0.05 |
1.79 |
0.37 |
0.011 |
0.023 |
20.15 |
9.52 |
0.008 |
0.09 |
Mechanical Properties of Deposited Metal
| Test Item |
Rm(Mpa) |
ReL(Mpa) |
A(%) |
KV2(J) |
| Typical |
580 |
- |
42 |
- |
Size & Recommended Current (AC/DC)
WA(A)=Welding Current (A)
| Dia(mm) |
φ2.5 |
φ3.2 |
φ4.0 |
φ5.0 |
| Current(A) |
80~140 |
250~350 |
350~450 |
400~500 |
X- ray Inspection: I
Instruction:
The wire should be kept in dry place.
The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away.
AWS A5.9 ER308L
Description: ER308L is a extra low carbon stainless steel wire, it is used for automatic submerged
welding combining with SJ601 arc.
Application: for welding extra low carbon Cr18Ni8 stainless steel.such as ship hulls, bridges. Pressure vessels as well as H-beam structures.
Chemical Composition of Welding Wire(%)
GV=Guarantee Value
| Test Item |
C |
Mn |
Si |
S |
P |
Cr |
Ni |
Mo |
Cu |
| GV |
≤0.03 |
1.0~2.5 |
0.3~0.65 |
≤0.03 |
≤0.03 |
19.5~22 |
9.0~11.0 |
≤0.75 |
≤0.75 |
| Typical |
0.023 |
1.76 |
0.51 |
0.019 |
0.018 |
19.92 |
9.56 |
0.1 |
0.11 |
Mechanical Properties of Deposited Metal
GV=Guarantee Value
| Test Item |
Rm(Mpa) |
ReL(Mpa) |
A(%) |
KV2(J) |
| GV |
≥520 |
- |
≥35 |
- |
| Typical |
592 |
- |
42 |
- |
Size & Recommended Current (AC/DC)
WA(A)=Welding Current (A)
| Dia(mm) |
φ2.5 |
φ3.2 |
φ4.0 |
φ5.0 |
| Current(A) |
80~140 |
250~350 |
350~450 |
400~500 |
X- ray Inspection: I
Instruction:
The wire should be kept in dry place.
The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away.
Products Picture:
Company Brief Introduction
(1)Company Name:Shandong Hulin Welding Material Co.,Ltd
(2)Main Products:
SAW Flux&Wire, MIG Wire, FCW wire.
(3)Best Selling Product Models:
SAW Flux:SJ101,SJ101G,SJ102,SJ301,SJ501,HJ107,HJ260,HJ431
SAW Wire: EM12K,EL8,EL12
MIG Wire: ER70S-6
FCW Wire: E71T-1
(5)Quality System:ISO9001:2000
(6)Year Established:1999
(7)Brand Name:Panding Brand
(8)Application: Steel Pipe, Structural steel, LPG Cylinder, Pressure vessel, Boiler, Bridges etc.
Packing & Shipping Details:
(1)Bag:25 KGS/Kraft Bag With Plastic Lining Inside
(2)Pallet:40 Bags(1 Ton)/Plywood Pallet
(3)Container:20-24 Tons/Container
(4)OEM & buyer label is ok, and technical support can be offered
Customers Feedback:
Audited Supplier 
Company Brief Introduction
){kind=link}
){kind=link}